High temperature gasket comparison table

High temperature gasket comparison

Lotfi Grine, Eng. – Product Specialist at Robco


High Temperature Gaskets

Gaskets made from elastomers achieve a seal at minimum mechanical load, because of their intrinsic low porosity. Elastomers are also added to enable fibrous-based gaskets to achieve good sealability.

However, even the best elastomers or polymers like silicone and PTFE cannot be used at continuous elevated temperatures, above 260°C (500°F), except for a few exotic and very expensive materials that can be used up to 325°C (650°F). What materials can you then choose from ? If we remove chemical resistance from the equation, it will depend mostly on 3 factors :

  1. maximum temperatures
  2. maximum pressure
  3. flange and bolting set-up.
This table lists these factors for the various gasket materials available:

Gasket Material

Continuous Temperature

Pressure

Load to obtain a seal

Sealability

 

Matériaux du joint

Température continue

Pression

Force pour étancher

Étanchéité

Glass fibers & HT silicone laminate / fibre de verre et silicone

315°C (600°F)

1.5 bar (25 psi)

Low / basse

medium / moyen

Homogeneous Flexible graphite / Graphite homogène

370°C (700°F)

41 bar (600 psi)

High / élevée

excellent

Serrated metallic & graphite Maxiprofile / joint métallique et graphite dentelé

480°C (900°F)

140 bar (2000 psi)

 high / élevée

excellent

Robco composite gasket / Joint composite Robco

900°C (1650°F)

2,4 bar (35 psi)

Low / basse

medium / moyen

Machined Inconel / Inconel usiné

900°C (1650°F)

345 bar (5000 psi)

very high / très élevée

excellent

Mineral fibers millboards / Cartons de fibres minérales

1000°C (1830°F)

0.69 bar (10 psi)

Low / basse

poor / faible

Mineral fiber papers (ceramic, biosoluble, etc.) / Papiers de fibres minérales

1100°C (2000°F)

0.35 bar (5 psi)

Low / basse

poor / faible

Homogeneous Flexible graphite in a vacuum or non-oxidizing environment / graphite – dans un environnement non-oxidant ou sous vide

1500°C (2730°F)

41 bar (600 psi)

High / élevée

excellent

 

 

Lotfi Grine, Ing. - Spécialiste produit chez Robco

Joint d’étanchéité pout températures élevées

Les joints en élastomères permettent d'obtenir une étanchéité avec une charge mécanique minimale, en raison de leur faible porosité intrinsèque. Des additifs élastomères sont également ajoutés pour permettre aux joints à base de fibres d'obtenir une bonne étanchéité.

Cependant, même les meilleurs élastomères et polymères comme le silicone et le PTFE ne peuvent pas être utilisés à des températures élevées continues, supérieures à 260°C (500°F), exception faite de quelques matériaux exotiques et onéreux, qui pourront atteindre 325°C (650°F). Quels matériaux pouvez-vous donc choisir? Si nous supprimons la résistance chimique de l'équation, cela dépendra de trois facteurs :

  1. température maximale
  2. pression maximale
  3. conception et assemblage des brides et boulons.
Le tableau ci-haut répertorie ces facteurs pour les différents matériaux de joints disponibles:


Labels:

Comments

Post a Comment

Popular posts from this blog

Seal Durability: How Temperature and Pressure Influence Performance

  Understanding the Impact of Temperature and Pressure on Seal Performance An In-depth Look at How Different Temperature and Pressure Conditions Affect the Performance and Lifespan of Various Sealing Materials In the world of industrial fluid sealing, understanding how temperature and pressure impact seal performance is crucial. Seals are designed to prevent leakage, ensuring that fluids remain contained within a system. However, the conditions under which they operate can significantly influence their effectiveness and longevity. Let's delve into how different temperature and pressure conditions affect the performance and lifespan of commonly used sealing materials. Temperature: The Heat Factor Temperature extremes can greatly influence seal performance. Both high and low temperatures can cause material deformation, chemical breakdown, and loss of elasticity, leading to seal failure. Here's how different materials react: 1. Elastomers: High Temperatures: Elastomers lik...
Post a Comment
Read more

6 raisons pour lesquelles vous avez besoin de couvertures chauffantes sur vos conteneurs de liquides industriels pendant l'hiver

    Les avantages des couvertures chauffantes pour les liquides industriels pendant les hivers rigoureux du Canada Lorsqu'il s'agit de gérer des liquides industriels pendant les rudes hivers canadiens, maintenir la bonne température est essentiel pour garantir l'efficacité et la sécurité. Que vous stockiez ou transportiez des produits chimiques, des huiles, des adhésifs ou d'autres matériaux sensibles dans des fûts, seaux ou cuves, les conditions de gel peuvent gravement affecter leur viscosité, leur utilisabilité et même causer des dommages irréversibles. Une solution pratique à ce problème est l'utilisation de couvertures chauffantes. Voici pourquoi elles sont indispensables pour les applications industrielles. 1. Prévention du gel et maintien du flux Les hivers canadiens apportent souvent des températures sous zéro, ce qui peut entraîner le gel des liquides industriels ou les rendre trop visqueux pour être efficacement utilisés. Les couvertures chauffantes ...
Post a Comment
Read more

Bolted flange joint assembly guidelines from ASME PCC1-2019

  ASME PCC1-2019 : technical notes about sealing performance Lotfi Grine, Eng. – Product Specialist at Robco   In the following technical notes, you will find valuable technical extracts from the ASME PCC1 2019 ( bolted flange joint assembly (BFJA) guidelines) to help better understand sealing behaviour and produce a positive seal. - Calculating Target Torque Values are based on the root area. The root areas are based on coarse-thread series for sizes 1 in. and smaller with 8-pitch thread series for sizes 1 1/8  in. and larger (Section H). - The major long-term value of coated bolts is to protect against corrosion of the exposed threads and to minimize break-out and nut-removal torque, thereby promoting ease of joint disassembly (Section 7). - Section VIII, Division 1 of the ASME Boiler and Pressure Vessel Code requires that nuts engage the threads for the full depth of the nut (Section 8.2).   - Start-up re-torque is performed when the temperature of ...
Post a Comment
Read more